Pouch Cell Film, D-EL40H(3)

Pouch Cell Film, D-EL40H(3) is available from ProDigitek, an Australian supplier, shipped within Australia.

Product Specifications

Model: D-EL40H (3)

Brand: Japanese DNP

Thickness (μm): 113

Features

a. Water vapor barrier

b. Electrolyte resistance (Sealing)

c. Electrolyte resistance (Laminating)

Steam Barrier Property (60°C90%RH 336H): < 50ppm

Initial strength of laminated layers(AL/PP): 10-11 N/15mm

Initial sealing strength(Sealing Pressure 0.5MPa, 190°C 3seconds): 80-90N/15mm

Initial sealing strength(Sealing Pressure 1.0MPa, 190°C 3seconds): 100-110N/15mm

Electrolyte resistance(Sealed film strength test 60°C 14days): <10N/15mm

Electrolyte resistance(Seal strength test with sealing pressure 0.5MPa, 190°C 3seconds): 70-80N/15mm

Electrolyte resistance(Seal strength test with sealing pressure 1.0MPa, 190°C 3seconds): 80-90N/15mm

Sealing strength in electrolyte(Sealing pressure 0.5MPa, 190°C 3seconds): 70-80N/15mm

Sealing strength in electrolyte(Sealing pressure 1.0MPa, 190°C 3seconds): 75-85N/15mm

Punch forming depth(Control raised surface pressure 0.17MPa, Size:80*120mm): >6.0mm

Water vapor barrier performance 60 °C 90% RH 336H: sealing surface pressure 1.0Mpa

Initial sealing strength: sealing surface pressure 0.5Mpa

190 °C, 3 seconds: sealing surface pressure 1.0Mpa

Electrolyte resistance (sealing strength test): sealing surface pressure 0.5Mpa

60 °C, 14days: sealing surface pressure 1.0Mpa

Sealing strength in electrolyte: sealing surface pressure 0.5Mpa

190 °C, 3 seconds: sealing surface pressure 1.0Mpa

Deep-drawing forming depth: Control the surface pressure of pleats 0.17Mpa (size: 80 * 120mm)

Typical Uses

Battery cell assembly and preparation in research laboratories

Laboratory consumables for battery research